INDUSTRIAL MINERALS| ORIGIN | : TURKEY, MOROCCO, SENEGAL, EGYPT, U.S.A (Subject to availability) |
| QUANTITIY | : 25,000MT TO 50,000MT |
| SHIPPING | : FOB/CFR |
R.P GRADE 1
| CHEMICAL COMPOSITION | |||
| Moisture | % W/W | 2.00 (Max) |
|
| Total Phosphate | P2o5 |
% W/W | 30 (Min) |
| Calcium Oxide | CaO |
% W/W | 45 – 52 |
| Sulphate | SO3 |
% W/W | 0.5 – 2 |
| Silica | SiO2 |
% W/W | 5 – 8 |
| Carbon-di-oxide | CO2 |
% W/W | 5 – 6 (Max ) |
| Floride | F |
% W/W | 4 (Max) |
| Iron | Fe2O3 |
% W/W | 1.0 (Max) |
| Iron and Aluminium | R2O3 |
% W/W | 2.0 (Max) |
| Water Soluble | CL |
% W/W | 0.04 (Max) |
| Sodium Oxide | Na2O |
% W/W | 0.8 (Max) |
| Potassium Oxide | K2O |
% W/W | 0.3 |
| Magnesium Oxide | Mgo |
% W/W | 0.5 (Max ) |
| Organic Matter with Crystalline | % W/W | 2.4 (Max) |
|
| B P L | 65.5 % Min |
||
| PHYSICAL COMPOSITION : | |||
| Fluidity | Free Flowing |
||
| Particle size distribution : |
|
||
| a. + Mesh | 4.75 mm |
% W/W | 0 – 2 |
| b. - 4 + 100 Mesh | 4.75 mm – 0.15 mm |
% W/W | 65 – 80 |
| c. -100+200 Mesh | 0.15mm-0.075 mm |
% W/W | 15 – 25 |
| d. -200+270 Mesh | 0.075mm – 0.053mm |
% W/W | 1 – 3 |
| e. - 270 Mesh | 0.053 mm |
% W/W | 2 – 3 |
R.P GRADE 2
| CHEMICAL COMPOSITION | |||
Moisture |
% W/W |
2.00 (Max) |
|
Total Phosphate |
P2o5 |
% W/W |
32.95 (Min) |
Calcium Oxide |
CaO |
% W/W |
48 – 52 |
Sulphate |
SO3 |
% W/W |
0.7 – 1.90 |
Silica |
SiO2 |
% W/W |
2.5 – 5 |
Carbon-di-oxide |
CO2 |
% W/W |
5 (Max ) |
Floride |
F |
% W/W |
4 (Max) |
Iron |
Fe2O3 |
% W/W |
1 (Max) |
Iron and Aluminium |
R2O3 |
% W/W |
2 (Max) |
Water Soluble |
CL |
% W/W |
0.04 (Max) |
Sodium Oxide |
Na2O |
% W/W |
0.2 – 0.8 |
Potassium Oxide |
K2O |
% W/W |
0.1 – 0.3 |
Magnesium Oxide |
Mgo |
% W/W |
0.5 (Max ) |
Organic Matter with Crystalline |
|
% W/W |
2.4 (Max) |
B P L |
|
|
72 % Min |
PHYSICAL COMPOSITION : |
|
|
|
Fluidity |
|
|
Free Flowing |
Particle size distribution : |
|
|
|
a. + Mesh |
4.75 mm |
% W/W |
0 – 2 % W/W |
b. - 4 + 100 Mesh |
4.75 mm – 0.15 mm |
% W/W |
65 – 80 % W/W |
c. -100+200 Mesh |
0.15mm-0.075 mm |
% W/W |
15 – 25 % W/W |
d. -200+270 Mesh |
0.075mm – 0.053mm |
% W/W |
1 – 3 % W/W |
e. - 270 Mesh |
0.053 mm |
% W/W |
2 – 3 % W/W |
R.P GRADE 3
| CHEMICAL COMPOSITION : |
|
|
|
|
Moisture |
105 C |
% W/W |
3.0 |
4.0 |
Total Phosphate |
P2o5 |
% W/W |
30 |
32 |
Calcium Oxide |
CaO |
% W/W |
50 |
52 |
Silica |
SiO2 |
% W/W |
2.5 |
3.5 |
Carbon-di-oxide |
CO2 |
% W/W |
5.5 |
7.0 |
Floride |
F |
% W/W |
3.0 |
4.0 |
Iron |
Fe2O3 |
% W/W |
0.2 |
0.4 |
Aluminium Oxide |
Al203 |
% W/W |
0.4 |
0.6 |
Sodium Oxide |
Na2O |
% W/W |
|
1.0 |
Potassium Oxide |
K2O |
% W/W |
|
0.2 |
Magnesium Oxide |
Mgo |
% W/W |
|
0.4 |
PHYSICAL COMPOSITION : |
|
|
|
|
Fluidity |
|
|
|
Free Flowing |
SIZE(DRY TYLER MESH) : |
|
|
|
|
a. + 4Mesh |
Quantity > 2% |
|
To be deducted from the B/L weight. |
|
| b. -100 to +270 mesh | Quantity >15% |
|
To be added to the quantity of -270 |
|
c. -270 mesh |
Quantity > 3% |
|
To be deducted from the B/L weight. |